Indentation and scratch testing of DLC-Zr coatings on ultrafine-grained titanium processed by high-pressure torsion
High-pressure torsion was employed to refine the microstructure of grade 2 Ti under an imposed pressure of 3.0 GPa at room temperature. The microhardness of grade 2 Ti increased from 1.82 GPa for the coarse grain state to 3.05 GPa after high-pressure torsion processing, where this value is very clos...