Optical and RBS studies in Tm implanted ZnO samples
We report on optical and structural analysis of Tm implanted ZnO [0001] single crystals. The samples were implanted at room temperature with 150 keV Tm+ ions with a nominal fluence of 5×1016 Tm +/cm2 and subsequently air annealed for 30 min at 800°C, 900°C and 950°C. The implantation damage and anne...
| Autor principal: | |
|---|---|
| Outros Autores: | , , , , , |
| Formato: | conferenceObject |
| Idioma: | eng |
| Publicado em: |
1000
|
| Assuntos: | |
| Texto completo: | http://hdl.handle.net/10773/6736 |
| País: | Portugal |
| Oai: | oai:ria.ua.pt:10773/6736 |
| Resumo: | We report on optical and structural analysis of Tm implanted ZnO [0001] single crystals. The samples were implanted at room temperature with 150 keV Tm+ ions with a nominal fluence of 5×1016 Tm +/cm2 and subsequently air annealed for 30 min at 800°C, 900°C and 950°C. The implantation damage and annealing effects were investigated with Rutherford Backscattering/Channelling Spectroscopy. We observe that following implantation the majority of Tm ions are incorporated on Zn sites. The optical properties of as-implanted and annealed samples have been studied by low temperature photoluminescence measurements. Well defined Tm-related near infrared emission were observed upon above band gap excitation and the data are consistent with the presence of multi Tm-related optical centers. |
|---|