Influence of fiber diameter and crystallinity on the stability of electrospun poly(L-lactic acid) membranes to hydrolytic degradation

Hydrolytic degradation of electrospun mats of poly(L-lactic acid), PLLA, as a function of crystallinity and fiber diameter has been studied. The degradation in a saline phosphate buffer solution (PBS) up to 20 weeks produced a slight decrease in the sample mass but a clear decrease of the polymer av...

ver descrição completa

Detalhes bibliográficos
Autor principal: Dias, J. C. (author)
Outros Autores: Ribeiro, C. (author), Sencadas, Vítor João Gomes Silva (author), Botelho, Gabriela (author), Gómez Ribelles, J. L. (author), Lanceros-Méndez, S. (author)
Formato: article
Idioma:eng
Publicado em: 2012
Assuntos:
Poly (L-lactic acid)
Electrospun nanofibers
In-vitro degradation
Viscosity average molecular weight
Science & Technology
Texto completo:http://hdl.handle.net/1822/22647
País:Portugal
Oai:oai:repositorium.sdum.uminho.pt:1822/22647
Descrição
Resumo:Hydrolytic degradation of electrospun mats of poly(L-lactic acid), PLLA, as a function of crystallinity and fiber diameter has been studied. The degradation in a saline phosphate buffer solution (PBS) up to 20 weeks produced a slight decrease in the sample mass but a clear decrease of the polymer average molecular weight in the amorphous fibers. The aforementioned effect decreases as crystallinity increases. Important for applications is that morphological characteristics of the membranes such as average fiber diameter and membrane porosity are also affected by the degradation process. Fiber diameter increases while membrane porosity decreases, resulting in closer packed fibers due to the release of internal tensions related to the electrospinning and/or thermal treatment processes.

Registros relacionados