| Summary: | The influence that ohmic heating technology and its associated moderate electric fields (MEF) have upon production of whey protein isolate cold-set gels mediated by iron addition was investigated. Results have shown that combining heating treatments (90 °C, 5 min) with different MEF intensities let hydrogels with distinctive micro and macro properties i.e. particle size distribution, physical stability, rheological behavior and microstructure. Resulting hydrogels were characterized (at nano-scale) by an intensity-weighted mean particle diameter of 145 nm, a volume mean of 240 nm. Optimal conditions for production of stable whey protein gels were attained when ohmic heating treatment at a MEF of 3 V cm 1 was combined with a cold gelation step using 33 mmol L 1 of Fe2 +. The consistency index of hydrogels correlated negatively to MEF intensity, but a shear thickening behavior was observed when MEF intensity was increased up to 10 V cm 1. According to transmission electron microscopy, ohmic heating gave rise to a more homogenous and compact fine-stranded whey protein-iron microstructure. Ohmic heating appears to be a promising technique, suitable to tailor properties of whey protein gels and with potential for development of innovative functional foods.
|
|---|