Magnetoelectric metglas/bidomain y + 140°-cut lithium niobate composite for sensing fT magnetic fields
We investigated the magnetoelectric properties of a new laminate composite material based on y+140°-cut congruent lithium niobate piezoelectric plates with an antiparallel polarized “head-to-head” bidomain structure and metglas used as a magnetostrictive layer. A series of bidomain lithium niobate c...
| Autor principal: | |
|---|---|
| Outros Autores: | , , , , , , , , |
| Formato: | article |
| Idioma: | eng |
| Publicado em: |
2020
|
| Assuntos: | |
| Texto completo: | http://hdl.handle.net/10773/27877 |
| País: | Portugal |
| Oai: | oai:ria.ua.pt:10773/27877 |
| Resumo: | We investigated the magnetoelectric properties of a new laminate composite material based on y+140°-cut congruent lithium niobate piezoelectric plates with an antiparallel polarized “head-to-head” bidomain structure and metglas used as a magnetostrictive layer. A series of bidomain lithium niobate crystals were prepared by annealing under conditions of Li2O outdiffusion from LiNbO3 with a resultant growth of an inversion domain. The measured quasi-static magnetoelectric coupling coefficient achieved |αE31| = 1.9 V·(cm·Oe)–1. At a bending resonance frequency of 6862 Hz, we found a giant |αE31| value up to 1704 V·(cm·Oe)–1. Furthermore, the equivalent magnetic noise spectral density of the investigated composite material was only 92 fT/Hz1/2, a record value for such a low operation frequency. The magnetic-field detection limit of the laminated composite was found to be as low as 200 fT in direct measurements without any additional shielding from external noises. |
|---|